VEGEMAT

The materials offered - Vegemat - are suitable for injection moulding and extrusion/thermoforming applications. Vegemat is offered by Plantaplast in the German-speaking area.

FIB AN 02M30

  • Compound filled with natural fibres
  • Developed for use in injection moulding
  • Food-safe
  • Good flowability
  • Very stiff and temperature-resistant due to filler content
  • Young´s modulus [GPa]  6,5 GPa
  • max. tension stress [MPa]  49 MPa
  • Charpy impact strength [kJ/m²]  8 kJ/m²

FIB AN 03K30

 
  • Compound filled with cellulose fibres
  • Developed for use in injection moulding
  • Food-safe
  • Increased stiffness due to filler content
  • Young´s modulus [GPa]  4,3 GPa
  • max. tension stress [MPa]  27 MPa
  • Charpy impact strength [kJ/m²]  8 kJ/m²

FLEX AN 01_45

  • Unfilled material
  • Developed for use in injection moulding
  • Food-safe
  • Good flowability
  • Translucent
  • Young´s modulus [GPa]  2,85 GPa
  • max. tension stress [MPa]  40 MPa
  • Charpy impact strength [kJ/m²]  23 kJ/m²

FLEX AN 02_35

  • Developed for use in injection moulding
  • Good flowability
  • High Charpy impact strength
  • Young´s modulus [GPa]  2,9 GPa
  • max. tension stress [MPa]  32 MPa
  • Charpy impact strength [kJ/m²]  30 kJ/m²

FLEX NN 04_50

  • Developed for use in injection moulding
  • Good flowability
  • Food-safe
  • Increased temperature resistance compared to FLEX 01_45
  • Partially crystalline material
  • Young´s modulus [GPa]  2,97 GPa
  • max. tension stress [MPa]  36 MPa
  • Charpy impact strength [kJ/m²]  14 kJ/m²
 

FLEX AN 01_10

  • Developed for the extrusion of flat foils for use in thermoforming
  • Food-safe
  • Properties comparable with injection moulding type FLEX 01_45
  • Translucent
  • Young´s modulus [GPa]  3 GPa
  • max. tension stress [MPa]  44 MPa
  • Charpy impact strength [kJ/m²]  23 kJ/m²

FLEX AN 4_15

  • Developed for the extrusion of foils for use in thermoforming
  • Food-safe
  • Properties comparable with injection moulding type FLEX 04_50
  • Increased temperature resistance compared to FLEX 01_10
  • Translucent
  • Young´s modulus [GPa]  2,83 GPa
  • max. tension stress [MPa]  37 MPa
  • Charpy impact strength [kJ/m²]  15 kJ/m²
 